第 47 卷第 6 期 Vol. 47 No. 6 2017 年 12 月 Dec 2017

所属栏目：功能材料 侧柏叶状ZnCo2O4的制备及其电化学性能研究

任 娜，酒红芳*，张少梅 （中北大学 理学院，山西 太原 030051）

摘　要：通过溶剂热法合成了ZnCo-醇酸盐前驱体，前驱体于空气中在一定的温度下煅烧处理得到侧柏叶状ZnCo2O4。使用X射线衍射（XRD）和扫描电子显微镜（SEM）对所制备的样品的物相组成、结构和形貌进行了表征与分析。研究结果表明，侧柏叶状ZnCo2O4用作锂离子电池负极材料时，具有较高的可逆容量、很好的循环稳定性以及优异的倍率性能。

关键词：锂离子电池；负极材料；侧柏叶；ZnCo2O4

中图分类号：TM919.2　　文献标识码：A　　文章编号：1009-9212（2017）06-0061-04

Preparation and Electrochemical Performances of Platycladus Orientalis Leaf Shaped ZnCo2O4

REN Na, JIU Hong-fang*, ZHANG Shao-mei (College of Science, North University of China, Taiyuan 030051, China)

Abstract：ZnCo-alcohol acid salt as a precursor was synthesized by solvent-thermal method, then the target product was obtained followed calcination under certain temperature in air. The crystalline phase, structure and morphology of the product were measured by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Using the platycladus orientalis leaf shaped ZnCo2O4 as raw material for lithium ion battery anode, it has a high reversible capacity, good circulation stability and excellent multiplier performance.

Key words：lithium ion battery; anode materials; platycladus orientalis leaf; ZnCo2O4