第 48 卷第 5 期 Vol. 48 No. 5 2018 年 10 月 Oct 2018

所属栏目：功能材料 5，5-联四唑-1，1-二氧二羟胺（TKX-50）球型化的研究

马凤利，吴晓青，白 宇，许 达，张 瑞，米登峰 （中北大学 理学院，山西 太原 030051）

摘　要：研究了溶剂-非溶剂法工艺技术条件对 TKX-50结晶形态的影响规律。结果表明，以二甲基砜（DMSO）为溶剂，温度为55℃、搅拌速度为300 r·min-1、非溶剂［v（溶剂 A）∶v（溶剂 B）=1∶1）］和滴加速度为20 min·mL-1的条件下，重结晶所得的TKX-50晶体形状规则、棱角少，且具有更好的热安定性。

关键词：DMSO；TKX-50；重结晶；球形化

中图分类号：TJ55；O6　　文献标识码：A　　文章编号：1009-9212（2018）05-0048-04

Spheroidization of 5,5'-Bistetrazole-1,1'-diolate Dihydroxylammonium

MA Feng-li, WU Xiao-qing, BAI Yu, XU Da, ZHANG Rui, MI Deng-feng (College of Science, North University of China, Taiyuan 030051, China)

Abstract：The effect of solvent-nonsolvent process conditions on the crystalline morphology of TKX-50 was studied. The results showed that TKX-50 crystals obtained by recrystallization had regular shape with fewer edges and corners, and better thermal stability under the conditions of temperature of 55℃, stirring speed of 300 r·min-1, non-solvent mixing ratio of 1∶1 and dropping acceleration of 20 min·mL-1.

Key words：DMSO; TKX-50; recrystallization; spheroidization

基金项目：新型含能化合物性能研究（1710800001HX）。

作者简介：马凤利（1992-），女，山西忻州人，硕士研究生，主要从事含能材料的研究（E-mail：1475238909@qq.com）。

联 系 人： 吴晓青，教授，主要从事含能材料的研究（E-mail：1369680249@qq.com）。

收稿日期： 2018-10-1